6mm Ultra-Thin Silicon Carbide Ceramic Tile with NIJ Level III Protection and High Density Microstructure
Détails sur le produit:
| Lieu d'origine: | Hunan, Chine |
| Nom de marque: | High Broad |
| Certification: | ISO 9001:2015, NIJ 0101.06 |
| Numéro de modèle: | tuiles sic |
| Documents: | SIC Ballistic Armor Tiles-P...ad.pdf |
Conditions de paiement et expédition:
| Quantité de commande min: | 1000 pièces |
|---|---|
| Prix: | USD 0.1-1 / Piece |
| Détails d'emballage: | Insert individuel en mousse EPE + sac antistatique scellé sous vide + caisse en contreplaqué d'e |
| Délai de livraison: | 5-7 jours ouvrables pour le stock, 15-20 jours pour la production |
| Conditions de paiement: | T/T, L/C, Western Union |
| Capacité d'approvisionnement: | 2500000 pièces par mois |
|
Détail Infomation |
|||
| Densité: | 3,12-3,18 g/cm³ | Dureté (GPa): | 25-28 |
|---|---|---|---|
| Résistance à la flexion: | 400-480 MPa | Taille des carreaux: | 100x100 mm |
| Densité en bits/pouce carré: | ≤28kg/m² | Résistance à la rupture: | 3,8-4,8 MPa·m½ |
| Mettre en évidence: | Ultra Thin SiC Tile,Lightweight Strike Face Plate,NIJ III Thin Armor Ceramic |
||
Description de produit
- 6mm Ultra-Thin Profile
- High Density Microstructure
The HB achieves NIJ Level III protection with just 6mm ceramic thickness—a 25% reduction from standard 8mm tiles. This is made possible through our advanced high-density pressureless sintering process that produces SiC with 3.15+ g/cm³ density and 2600+ HV hardness, approaching hot-pressed density values without the associated cost premium. The result: armor systems that are significantly lighter and thinner without compromising protection.
| Ceramic Type | Required Thickness | Areal Density @ NIJ III | Weight Index |
|---|---|---|---|
| HB SiC (6mm high-density) | 6.0 mm | ≤ 28 kg/m² | ★★★ Best |
| Standard SiC (8mm) | 8.0 mm | ~36 kg/m² | ★★ Good |
| Alumina Al2O3 (10mm) | 10.0 mm | ~42 kg/m² | ★ Heavy |
| Boron Carbide B4C (6mm) | 6.0 mm | ~22 kg/m² | ★★★★ Lightest (High Cost) |
WNRLN 6mm SiC achieves the optimal balance: B4C-level thinness at 50-60% lower cost.
Our controlled-atmosphere pressureless sintering process achieves 98.5%+ theoretical density with minimal porosity (<0.5%), enabling the thinner profile without strength compromise.
The 6mm ultra-thin profile and 28 kg/m² areal density make this tile ideal for helicopter crew seats, vehicle spall liners, and portable shield applications where weight budget is critical.
Double-side ground to ≤20μm flatness and ≤0.8μm Ra surface finish, ensuring uniform adhesive bond line thickness across the entire tile surface.
Despite the thin profile, enhanced fracture toughness (3.8-4.8 MPa*m½) ensures reliable multi-hit performance. Tested with 3-round triangular shot pattern at 50mm spacing.
Technical datasheets and ballistic test reports available